SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL32B225KCJSNNE Product : Multi-layer Ceramic Capacitor Description : CAP, 2.2, 100V, 10%, X7R, 1210 A. Samsung Part Number Series Size CL 32 B 225 K C J S N N E Samsung Multi-layer Ceramic Capacitor 1210 (inch code) Dielectric X7R Capacitance 2.2 10 % Capacitance L: 3.2 0.3 100 V Thickness 2.5 0.2 mm 2.5 0.2 W: Termination Ni Metal Epoxy Plating Sn 100% Inner electrode tolerance Rated Voltage mm mm (Pb Free) Product Normal Special Reserved for future use Packaging Embossed Type, 7"reel(1,000ea) B. Samsung Reliability Test and Judgement condition Performance 1.00.2Vrms More than 100Mohm Rated Voltage 60~120 sec. Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Visual inspection 200% of the rated voltage Voltage mechanical breakdown Temperature X7R Characteristics Adhesive Strength (From -55 to 125, Capacitance change should be within 15%) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan (DF) Insulation Within specified tolerance Test condition 110% Capacitance 0.1 max. Resistance within 12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Performance Vibration Test Capacitance change : within 5% Tan , IR : initial spec. Moisture Capacitance change : Resistance Tan : 0.125 max IR Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours 3 direction (x, y, z) within 12.5% With rated voltage 402, 90~95%RH, 500+12/-0 hours : More than 12.5* High Temperature Capacitance change : Resistance Tan : 0.125 max IR Test condition within 12.5% With 150% of the rated voltage Max. operating temperature : More than 25* 1000+48/-0 hours Temperature Capacitance change : Cycling Tan , IR : initial spec. within 7.5% 1 cycle condition Min. operating temperature 25 25 Max. operating temperature 5 cycles test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.