SPECIFICATION
• Supplier : Samsung electro-mechanics • Samsung P/N : CL43A476MQJNNNE
• Product : Multi-layer Ceramic Capacitor •Description : CAP, 47㎌, 6.3V, ±20%, X5R, 1812
CL 43 A 476 M Q J N N N E
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 1812 (inch code) L: 4.5 ± 0.4 mm W: ± 0.3 mm
③Dielectric X5R ⑧Inner electrode
④Capacitance 47 ㎌Termination
⑤Capacitance ±20 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 6.3 V ⑩Special Reserved for future use
⑦Thickness 2.5 ± 0.2 mm ⑪Packaging Embossed Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Capacitance Within specified tolerance 120㎐±20% 0.5±0.1Vrms
Tan δ (DF) 0.1 max.
Insulation 10,000Mohm or 100Mohm⋅㎌Rated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (×10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X5R
Characterisitcs (From -55℃ to 85℃, Capacitance change shoud be within ±15%)
Adhesive Strength No peeling shall be occur on the 500g⋅F, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface 1) Sn63Pb37 solder
is to be soldered newly 235±5℃, 5±0.5sec.
2) SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Sn 100%
Cu
Ni
Test condition
250%
A. Samsung Part Number
3.2
Performance
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours × 3 direction (x, y, z)
Humidity Capacitance change : within ±12.5% 40±2℃, 90~95%RH, 500+12/-0hrs
Tan δ : 0.125 max
IR : 25㏁·㎌ or Over
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0hrs
IR : 12.5㏁·㎌ or Over
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : 25㏁·㎌ or Over
1000+48/-0hrs
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperatur
e
→25℃
→Max. operating temperature →25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
150%
Performance Test condition