SPECIFICATION * Supplier : Samsung electro-mechanics * Samsung P/N: CL05A225MQ5NSNC * Product : Multi-layer Ceramic Capacitor * Description : CAP, 2.2, 6.3V, 20%, X5R, 0402 A. Samsung Part Number Series CL 05 A 225 M Q 5 N S N C Samsung Multi-layer Ceramic Capacitor Size 0402 (inch code) Dielectric X5R Capacitance Capacitance L: 1.0 0.07 0.5 W: 0.07 mm Inner electrode Ni Termination Cu Plating Sn 100% 2.2 20 % tolerance mm (Pb Free) Product 0402 Size dimension Spec. Rated Voltage 6.3 V Special Reserved for future use Thickness 0.5 0.07 mm Packaging Cardboard Type, 7" reel B. Samsung Reliablility Test and Judgement condition Judgement 0.50.1Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 100Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (x10) 250% of the rated voltage Voltage mechanical breakdown Temperature X5R Characterisitcs Adhesive Strength (From -55 to 85, Capacitance change shoud be within 15%) No peeling shall be occur on the 500g*F, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan (DF) Insulation Within specified tolerance Test condition 110% Capacitance 0.1 max. within 12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface 1) Sn63Pb37 solder is to be soldered newly 2355, 50.5sec. 2) SnAg3.0Cu0.5 solder 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Judgement Vibration Test Capacitance change : within 5% Tan , IR : initial spec. Humidity Capacitance change : Test condition Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours x 3 direction (x, y, z) within 12.5% 402, 90~95%RH, 500+12/-0hrs Tan 0.125 max IR : 25* or Over Moisture Capacitance change : Resistance Tan 0.125 max IR : within 12.5% With rated voltage 402, 90~95%RH, 500+12/-0hrs 12.5* or Over within 12.5% With 100% of the rated voltage High Temperature Capacitance change : Resistance Tan 0.125 max Max. operating temperature IR : 1000+48/-0hrs 25* or Over Temperature Capacitance change : Cycling Tan , IR : initial spec. within 7.5% 1 cycle condition Min. operating temperature 25 Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.