SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL10A226MQ8NRNC Product : Multi-layer Ceramic Capacitor Description : CAP, 22, 6.3V, 20%, X5R, 0603 A. Samsung Part Number Series CL 10 A 226 M Q 8 N R N C Samsung Multi-layer Ceramic Capacitor Size 0603 (inch code) Dielectric X5R Capacitance Capacitance L: 1.6 0.2 Rated Voltage 6.3 V Thickness 0.8 0.2 mm 0.8 0.2 W: Inner electrode Ni Termination Cu Plating Sn 100% 22 20 % tolerance mm mm (Pb Free) Product 0603 Size dimension spec Special Reserved for future use Packaging Cardboard Type, 7" reel B. Samsung Reliability Test and Judgement condition Performance 0.50.1Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 50Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (10) 250% of the rated voltage Voltage mechanical breakdown Temperature X5R Characterisitcs Adhesive Strength (From -55 to 85, Capacitance change should be within 15%) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Tan (DF) Insulation Within specified tolerance Test condition 12020% Capacitance 0.1 max. within 12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat Tan , IR : initial spec. within 7.5% Solder pot : 2705, 101sec. Performance Vibration Test Capacitance change : within 5% Test condition Amplitude : 1.5mm Tan , IR : initial spec. From 10 to 55 (return : 1min.) Moisture Capacitance change : 2hours 3 direction (x, y, z) With rated voltage Resistance Tan : IR : 0.25 max 402, 90~95%RH, 500+12/-0hrs 8.8* or Over High Temperature Capacitance change : Resistance Tan : IR : within 12.5% within 12.5% 0.25 max With 100% of the rated voltage Max. operating temperature 17.7* or Over 1000+48/-0hrs Temperature Capacitance change : Cycling Tan , IR : initial spec. within 10% 1 cycle condition Min. operating temperature 25 25 Max. operating temperature 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.