SPECIFICATION
Supplier : Samsung electro-mechanics Samsung P/N : CL10Y105MR5NJNC
Product : Multi-layer Ceramic Capacitor Description : CAP, 1㎌, ±20%, 4V, X7S, 0603
CL 10 Y105 M R 5 N J N C
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 0603 (inch code) L: 1.6 ± 0.1 mm W: ± 0.1 mm
③Dielectric X7S ⑧Inner electrode
④Capacitance 1㎌Termination
⑤Capacitance ±20 % Plating (Pb Free)
tolerance ⑨Product SLIC
⑥Rated Voltage 4V ⑩Special Reserved for future use
⑦Thickness 0.5 +0.05/-0.1 mm ⑪Packaging Cardboard Type,7"reel(4,000ea)
A. Samsung Part Number
0.8
Ni
Cu
Sn 100%
B. Samsung Reliability Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 0.5±0.1Vrms
Tan δ (DF) 0.12 max.
Insulation More than 50Mohm㎌Rated Voltage 60~120 sec.
Resistance
Appearance No abnormal exterior appearance Visual inspection
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X7S
Characteristics (From -55℃ to 125℃, Capacitance change should be within ±22%)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
250%
Performance Test condition
Vibration Test Capacitance change : within ±20% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.2 max 40±2℃, 90~95%RH, 500+12/-0 hours
IR : More than 12.5㏁·㎌
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.2 max Max. operating temperature
IR : More than 25㏁·㎌
1000+48/-0 hours
Temperature Capacitance change : within ±12.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
Performance Test condition
150%