SPECIFICATION
Supplier : Samsung electro-mechanics Samsung P/N : CL31C100JHFNFNE
Product : Multi-layer Ceramic Capacitor Description : CAP, 10㎊, 630V, ±5%, C0G, 1206
CL 31 C100 J H F N F N E
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 1206 (inch code) L: 3.2 ± 0.15 mm W: ± 0.15 mm
③Dielectric C0G ⑧Inner electrode
④Capacitance 10 ㎊Termination
⑤Capacitance ±5 %Plating (Pb Free)
tolerance ⑨Product Product for POWER application
⑥Rated Voltage 630 V ⑩Special Reserved for future use
⑦Thickness 1.25 ± 0.15 mm ⑪Packaging Embossed Type,7"reel(2,000ea)
Ni
Cu
Sn 100%
A. Samsung Part Number
1.6
B. Samsung Reliability Test and Judgement condition
Capacitance Within specified tolerance 1㎒±10% 0.5~5Vrms
Q600 min
Insulation More than 500Mohm㎌500±50 Vdc 60~120 sec.
Resistance
Appearance No abnormal exterior appearance Visual inspection
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature C0G
Characteristics (From -55℃ to 125℃, Capacitance change should be within ±30PPM/℃)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±0.5㎊Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±0.25㎊Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Performance Test condition
150%
Vibration Test Capacitance change : within ±0.25㎊Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±0.75㎊With rated voltage
Resistance Q : 133.33 min 40±2℃, 90~95%RH, 500 +12/-0 hours
IR : More than 25㏁·㎌
High Temperature Capacitance change : within ±0.3㎊Wit
h
of the rated voltage
Resistance Q : 300 min Max. operating temperature
IR : More than 50㏁·㎌1000+48/-0 hours
Temperature Capacitance change : within ±0.25㎊1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
120%
Performance Test condition