R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 1/9 sheet 190-1 A4
spec.doc Phycomp Taiwan Ltd.
MULTILAYER CERAMIC ANTENNA (LINEAR POLARIZATION MODE)
1.88 GHz ~2.1 GHz
Product Specification1 (Preliminary)
QUICK REFERENCE DATA
Dimension 8.8* 6.8 * 0.9 mm
Working Frequency 1.88~2.1 GHz
Gain 2 dBi Max
VSWR 2 max
Polarization Linear
Azimuth Omni-directional
Impedance 50Ω
Operating Temperature -55~125 oC
Termination Ni/Sn (Environmentally-Friendly Leadless)
Resistance to soldering heat 260oC, 10 sec.
Special Environmental Concerns- Green Products Design: The foil making process is
using environmentally friendly aqueous solvent technology. Termination is lead free and
packing materials can be re-cycled
1 All the technical data and information contained herein are subject to change without prior notice
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 2/9 sheet 190-2 A4
spec.doc Phycomp Taiwan Ltd.
APPLICATION
DIMENSIONAL DATA
Figure Dimension Port
w
L
s1
T
s1
s1 F
C
C
s1
Fs1
T
s1
C
S2
s2
s1
w
L
s1
T
s1
s1 F
C
C
s1
Fs1
T
s1
C
S2
s2
s1
L
W
T
F
C
S1
S2
8.8±0.2mm
6.8±0.2mm
0.9±0.2mm
4.3±0.2mm
0.5±0.3mm
1.3±0.2mm
4.3±0.2mm
-
-
-
Feed termination
-
Solder termination
Solder termination
50ΩTransmission Line
Ground plane (back side)
DECT
Antenna
RF
Module
1mm
9 mm
8mm
8mm
Suggested Layout
Clearance
(no ground plane)
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 3/9 sheet 190-3 A4
spec.doc Phycomp Taiwan Ltd.
SOLDER LAND PATTERN
Figure Dimensions
(mm)
Remark
L
CC
F*
F
S1
S1
S2
S1
W
L
CC
F*
F
S1
S1
S2
S1
W
L
W
F
F*
C
S1
S2
10.00 ± 0.10
7.00 ± 0.10
1.40 ± 0.10
1.40 ± 0.10
0.90 ± 0.10
1.40 ± 0.10
1.40 ± 0.10
Feed Pad
Feed Pad (Optional)
NC Mount Pad Only
NC Mount Pad Only
Radiation Pattern
-90
-45
0
45
90
135
180
225
-90
-45
0
45
90
135
180
225
E Plane (ZY Plane) & H Plane (XY Plane) X
Z
Y
X
Z
Y
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 4/9 sheet 190-4 A4
spec.doc Phycomp Taiwan Ltd.
RELIABILITY DATA (Reference to IEC Specification)
IEC
384-10/
CECC 32
100
CLAUSE
IEC
6006868-2
TEST
METHOD
TEST PROCEDURE REQUIREMENTS
4.4 Mounting The antenna can be
mounted on printed-
circuit boards or ceramic
substrates by applying
wave soldering, reflow
soldering (including
vapour phase soldering)
or conductive adhesive
No visible damage
4.5 Visual inspection
and dimension
check
Any applicable method
using ´ 10
magnification
In accordance with
specification (no chip
off 3 mm)
4.8 Adhesion A force of 5 N applied
for 10 s to the line
joining the terminations
and in a plane parallel to
the substrate
No visible damage
4.9 Bond strength of
plating on end face
Mounted in accordance
with CECC 32 100,
paragraph 4.4
No visible damage
Conditions: bending 0.5
mm at a rate of 1mm/s,
radius jig. 340 mm,
1 mm warp on FR4
board of 90 mm length
No visible damage
4.10 Tb Resistance to
soldering heat
260 ± 5 °C for 10 ± 0.5 s
in a static solder bath
The terminations
shall be well tinned
after recovery and
Central Freq. Change
± 6%
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 5/9 sheet 190-5 A4
spec.doc Phycomp Taiwan Ltd.
IEC
384-10/
CECC 32
100
CLAUSE
IEC
6006868-2
TEST
METHOD
TEST PROCEDURE REQUIREMENTS
Resistance to
leaching
260 ± 5 °C for 30 ± 1 s
in a static solder bath
Using visual
enlargement of ´ 10,
dissolution of the
termination shall not
exceed 10%
4.11 Ta Solderability Zero hour test, and test
after storage (20 to 24
months) in original
atmosphere; un-mounted
chips completely
immersed for 2 ± 0.5 s
in 235 ± 5°C.
The termination must
be well tinned, at
least 75% is well
tinned at termination
4.12 Na Rapid change of
temperature
-55 °C (30 minutes) to
+125 °C (30 minutes);
100 cycles
No visible damage
Central Freq. Change
± 6%
4.14 Ca Damp heat 500 ± 12 hours at 60 °C;
90 to 95 % RH
No visible damage
2 hours recovery
Central Freq. Change
± 6%
4.15 Endurance 500 ± 12 hours at 125
°C;
No visible damage
2 hours recovery
Central Freq. Change
± 6%
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 6/9 sheet 190-6 A4
spec.doc Phycomp Taiwan Ltd.
ORDERING INFORMATION: 12NC Ordering Code
The DECT antennas may be ordered by using the 12 NC ordering code. These code numbers
can be determined by the following rules:
4311 1 12 00 188
F C M S T A
F. Family Code C. Packing Type Code
43 = Antenna 11 = 180 mm/ 7" blister (1000pcs)
M. Materials Code 13 = 330 mm/ 13”blister (4000pcs)
1 = High Frequency Material
S. Size Code
12 = 8.8*6.8 * 0.9 mm
T. Tolerance
00 = 100 M Hz Band Width
A. Working Frequency
188 = 1.88 GHz~2.1GHz
Example: 12NC 4311 112 00188
Product description: Antenna (43) by 1000 pcs (11) of High Frequency
Material (1), Size 8.8*6.8*0.9 mm (12);
Tolerance (00) of 100 MHz (VSWR<2)
Working Frequency (188) = 1.88G~2.1GHz Hz
ORDERING INFORMATION: Method II- by Clear Text Code
The antennas may be ordered by using the 16-digit clear text ordering code. These code
numbers can be determined by the following rules:
AN1880000788681K (Clear Text Code Example)
AN 1880 00 07 8868 1 K
Product Central Freq. Bandwidth Material Size Quantities Packing
AN=
Antenna
1880=1.80GHz
~ 2.1GHz
00= >100MHz 07=K7
8868=8.8*6.8*
0.9 mm
1 = 1K K=7" plastic
F =13" plastic
B = Bulk
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 7/9 sheet 190-7 A4
spec.doc Phycomp Taiwan Ltd.
Blister Tape Specifications
DIMENSION:
Serial no Checking note Index Spec(mm)
1Sprocket hole Do 1.55±0.10
2Pocket hole D1 1.50±0.10
3Distance sprocket hole/sprocket hole Po 4.0±0.10
4Distance pocket/pocket P1 12.0±0.10
5Distance sprocket hole/pocket P2 2.0±0.10
6Tape width W16.0±0.30
7Distance sprocket hole/outside E1.75±0.10
8Distance sprocket hole/pocket F7.50±0.10
9Pocket length Ao 7.45±0.10
10 Pocket length Bo 9.30±0.10
11 Pocket depth Ko 1.35±0.10
12 Thickness of tape T0.25±0.10
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 8/9 sheet 190-8 A4
spec.doc Phycomp Taiwan Ltd.
7”(180mm) Reel Specifications
Product size
code
Units per
Reel
Tape Width
(mm)
C
(mm)
D
(mm)
W1
(mm)
W2
(mm)
Antenna 1000 16 180.0±1.0 62±0.5
16.0+1
-0
20.5±0.2
R&D Print date 02/06/03 Preliminary use only
Nov. 20, 01
Multilayer Ceramic Antenna
for 1.88GHz~2.1GHz
4311 112 00188 Dec. 13, 01
Jan. 7, 02
Cliff Wang, Ph.D. 2002-01-07 Page 9/9 sheet 190-9 A4
spec.doc Phycomp Taiwan Ltd.
13”(330mm) Reel Specifications
Product size
code
Units per
Reel
Tape Width
(mm)
C
(mm)
D
(mm)
W1
(mm)
T
(mm)
Antenna 4000 16 330±0.10 100±0.1 16.5±0.10 2.3±0.1