CL05A105KP5NNNC - Samsung Electro-Mechanics

SPECIFICATIO

(Reference sheet)

 Supplier : Samsung electro-mechanics  Samsung P/N: CL05A105KP5NNNC

 Product : Multi-layer Ceramic Capacitor Description : CAP, 1㎌, 10V, ±10%, X5R, 0402

CL 05 A 105 K P 5 N N N C

① ②③ ④ ⑤ ⑥ ⑦⑧⑨⑩⑪

①Series Samsung Multi-layer Ceramic Capacitor

②Size 0402 (inch code) L: 1.0 ± 0.05 mm W: ± 0.05 mm

③Dielectric ⑧Inner electrode

④Capacitance 1㎌Termination

⑤Capacitance ±10 % Plating (Pb Free)

tolerance ⑨Product Normal

⑥Rated Voltage 10 V ⑩Special Reserved for future use

⑦Thickness 0.5 ± 0.05 mm ⑪Packaging Cardboard Type, 7" reel

B. Samsung Reliability Test and Judgement condition

Capacitance Within specified tolerance 1㎑±10% 1.0±0.2Vrms

Tan δ (DF) 0.1 max.

Insulation 10,000Mohm or 100Mohm㎌Rated Voltage 60~120 sec.

Resistance Whichever is Smaller

Appearance No abnormal exterior appearance Microscope (×10)

Withstanding No dielectric breakdown or of the rated voltage

Voltage mechanical breakdown

Temperature X5R

Characteristics (From -55℃ to 85℃, Capacitance change should be within ±15%)

Adhesive Strength No peeling shall be occur on the 500g·F, for 10±1 sec.

of Termination terminal electrode

Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)

with 1.0mm/sec.

Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder

is to be soldered newly 245±5℃, 3±0.3sec.

(preheating : 80~120℃ for 10~30sec.)

Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.

Soldering heat Tan δ, IR : initial spec.

Sn 100%

250%

Judgement Test condition

X5R

A. Samsung Part Number

0.5

Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm

Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)

2hours × 3 direction (x, y, z)

Moisture Capacitance change : within ±12.5% With rated voltage

Resistance Tan δ 0.2 max 40±2℃, 90~95%RH, 500+12/-0hrs

IR : 12.5㏁·㎌ or Over

High Temperature Capacitance change : within ±12.5% Wit

of the rated voltage

Resistance Tan δ 0.2 max Max. operating temperature

IR : 25㏁·㎌ or Over 1000+48/-0hrs

Temperature Capacitance change : within ±7.5% 1 cycle condition

Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃

→Max. operating temperature →25℃

5 cycle test

C. Recommended Soldering method :

Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )

Product specifications included in the specifications are effective as of March 1, 2013.

Please be advised that they are standard product specifications for reference only.

We may change, modify or discontinue the product specifications without notice at any time.

So, you need to approve the product specifications before placing an order.

Should you have any question regarding the product specifications,

please contact our sales personnel or application engineers.

150%

Judgement Test condition