SPECIFICATION Supplier : Samsung electro-mechanics Samsung P/N : CL31C470JIFNFNE CAP, 47, 1000V, 5%, C0G, 1206 Description : Product : Multi-layer Ceramic Capacitor A. Samsung Part Number Series CL 31 C 470 J I F N F N E Samsung Multi-layer Ceramic Capacitor Size 1206 Dielectric C0G (inch code) L: 3.2 0.15 47 5 % Capacitance Capacitance tolerance mm 1.6 0.15 mm W: Inner electrode Ni Termination Cu Plating Sn 100% (Pb Free) Product Product for POWER application Rated Voltage 1000 V Special Reserved for future use Thickness 1.25 0.15 mm Packaging Embossed Type, 7" reel B. Samsung Reliablility Test and Judgement condition Performance 0.5~5Vrms 50050 Vdc 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (10) 120% of the rated voltage Voltage mechanical breakdown Temperature C0G Characterisitcs Adhesive Strength (From -55 to 125, Capacitance change shoud be within 30PPM/) No peeling shall be occur on the 500gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. Solderability within 5% or 0.5 whichever is larger More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. Q Insulation Within specified tolerance Test condition 110% Capacitance 1000 min (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec. Solder pot : 2705, 101sec. Performance Test condition Vibration Test Capacitance change : High Temperature within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours 3 direction (x, y, z) Capacitance change : With 100% of the rated voltage Resistance within 3% or 0.3 whichever is larger Q: 350 min IR : Amplitude : 1.5mm Max. operating temperature 1000+48/-0hrs 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : Cycling 1 cycle condition within 2.5% or 0.25 whichever is larger Min. operating temperature Tan , IR : initial spec. Max. operating temperature 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue. 25 25