SPECIFICATION (Reference sheet)
Supplier : Samsung electro-mechanics Samsung P/N : CL05B472KB5NNND
Product : Multi-layer Ceramic Capa citor Description : CAP, 4.7㎋, 50V, ±10%, X7R, 0402
CL 05 B472 K B 5 N N N D
① ②③ ④ ⑤⑥⑦ ⑧ ⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 0402 (inch code) L: 1.0 ± 0.05 mm W: ± 0.05 mm
③Dielectric X7R ⑧Inner electrode
④Capacitance 4.7 ㎋Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 50 V ⑩Special Reserved for future use
⑦Thickness 0.5 ± 0.05 mm ⑪Packaging Cardboard Type, 13" reel
B. Samsung Reliability Test and Judgement condition
A. Samsung Part Number
Sn 100%
Cu
Ni
0.5
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2Vrms
Tan δ (DF) 0.025 max.
Insulation 10,000Mohm or 500Mohm㎌Rated Voltage 60~120 sec.
Resistance Whichever is Smaller
Appearance No abnormal exterior appearance Microscope (10)
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X7R
Characteristics (From -55℃ to 125℃, Capacitance change should be within ±15%)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Performance Test condition
250%
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.05 max 40±2℃, 90~95%RH, 500+12/-0hrs
IR : 25㏁·㎌ or Over
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.05 max Max. operating temperature
IR : 50㏁·㎌ or Over
1000+48/-0hrs
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
Product specifications included in the specifications are effective as of March 1, 2013.
Please be advised that they are standard product specifications for reference only.
We may change, modify or discontinue the product specifications without notice at any time.
So, you need to approve the product specifications before placing an order.
Performance Test condition
200%
Should you have any question regarding the product specifications,
please contact our sales personnel or application engineers.