SPECIFICATION * Supplier : Samsung electro-mechanics * Samsung P/N : CL21B332KCANNNC * Product : Multi-layer Ceramic Capacitor * Description : CAP, 3.3, 100V, 10%, X7R, 0805 A. Samsung Part Number CL Series Size Dielectric Capacitance Capacitance tolerance Rated Voltage Thickness 21 B 332 K C Samsung Multi-layer Ceramic Capacitor 0805 (inch code) L: 2.0 0.1 X7R 3.3 10 % 100 V 0.65 0.1 mm A N N mm Inner electrode Termination Plating Product Special Packaging N W: C 1.25 0.1 mm Ni Cu Sn 100% (Pb Free) Normal Reserved for future use Cardboard Type, 7" reel B. Samsung Reliablility Test and Judgement condition Capacitance Tan (DF) Insulation Resistance Appearance Withstanding Voltage Temperature Characterisitcs Adhesive Strength of Termination Bending Strength Solderability Resistance to Soldering heat Performance Test condition Within specified tolerance 1.00.2Vrms 110% 0.025 max. Rated Voltage 605 sec. 10,000Mohm or 500Mohm Whichever is Smaller No abnormal exterior appearance Microscope (x10) 200% of the rated voltage No dielectric breakdown or mechanical breakdown X7R (From -55 to 125, Capacitance change shoud be within 15%) No peeling shall be occur on the 500gF, for 101 sec. terminal electrode Capacitance change : within 12.5% Bending to the limit (1mm) with 1.0mm/sec. More than 95% of terminal surface 1) Sn63Pb37 solder is to be soldered newly 2355, 50.5sec. 2) SnAg3.0Cu0.5 solder 2455, 30.3sec. (preheating : 80~120 for 10~30sec.) Capacitance change : within 7.5% Solder pot : 2705, 101sec. Tan , IR : initial spec. Vibration Test Humidity Moisture Resistance High Temperature Resistance Temperature Cycling Performance Capacitance change : within 5% Tan , IR : initial spec. Test condition Amplitude : 1.5mm From 10 to 55 (return : 1min.) 2hours x 3 direction (x, y, z) within 12.5% 402, 90~95%RH, 500+12/-0hrs Capacitance change : Tan : 0.05 max IR : 1000Mohm or 50Mohm Whichever is Smaller Capacitance change : within 12.5% Tan : 0.05 max IR : 500Mohm or 25Mohm Whichever is Smaller Capacitance change : within 12.5% Tan : 0.05 max IR : 1000Mohm or 50Mohm Whichever is Smaller Capacitance change : within 7.5% Tan , IR : initial spec. With rated voltage 402, 90~95%RH, 500+12/-0hrs With 200% of the rated voltage Max. operating temperature 1000+48/-0hrs 1 cycle condition Min. operating temperature 25 Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 2505, 6sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.