Suppli e r : S a m s ung E lectro- Mechani c s CL05Y105KP6VPNC
Product : Multi-la yer Ce rami c Capa c i t or CAP, 1 , 10V, ± 10%, X7S, 0402
AEC-Q200 Qualified
A. Dim e ns i on
Dimension
B. Sam s ung Pa rt Number
CL 05 Y K P 6 V P N C
Series Sams ung Mult i-layer Ceramic Capacitor
Size (inch code) L : 1.00±0.20 mm W
:
0.50±0.20 mm
Dielectric Inner electrode Ni
Capacitance Termination Metal-Epoxy
Capacitance ± 10% Plating Sn 100% (Pb Free)
tolerance Product Automotive
Rated Voltage VSpecial code Normal
Thickness 0.50±0.20 mm Packaging Cardboard Type, 7" Reel
C. Reliability Test and Judgement condition
Test items
High Temperature Appearance : No abnormal exterior appearance Unpowered, 1,000hrs @ Max. tem perat ure
Exposure Capacitance Change W i t hin ±10 % Measurement at 24± 2hrs af t er test conclusion
0.2 max.
IR More than 10,000 or 50 ×Initial Measurement 2*
W hic hever is sm aller Final Measurement 3*
Temperature Cycling Appearance : No abnormal exterior appearance 1,000Cycles
Capacitance Change Within ±10 % Initial Measurem ent 2*
0.2 max. Final Measurement 3*
IR More than 10,000 or 50 ×Measurement at 24±2hrs after t es t conc lus ion
W hic hever is smaller 1 cycle condition : -55+0/-3 (30±3min) Room Temp. (1min)
Destructive Physical No Defects or abnorm alities Per EIA 469
Analysis
Humidity Bias Appearance : No abnormal exterior appearance 1,000hrs 85 /85%RH, Rated Voltage and 1.3~1.5V,
Capacitance Change Within ±12.5 % Add 100kohm resist or
0.2 max. Initial Measurement 2*
IR More than 500 or 5 ×Final Measurement 4*
W hic hever is smaller Measurement at 24± 2hrs af t er t es t conc lus ion
The charge/discharge current is les s t han 50mA.
High Temperature Appearance : No abnormal exterior appearance 1,000hrs @ 125 , 150% Rated Voltage,
Operating Life Capacitance Change Within ±12.5 % Initial Measurement 2*
0.2 max. Final Measurement 4*
IR More than 1,000 or 5 ×Measuremen t at 24± 2hrs af t er t es t conc lus ion
W hic hever is smaller The charge/discharge current is les s than 50mA.
X7S
Performance Test condition
10
0402
1
0.50±0.20 mm
Specification of Automotive MLCC (Reference sheet)
105
L
W
T
Samsung P / N :
Description :
0.25±0.10 mmBW
Size 0402 inch
1.00±0.20 mm
0.50±0.20 mm
External Visual No abnormal exterior appearance Microscope (X10)
Physical Dimension
s
W i t hin the s pec if ied dimens ions Using The calipers
Mechanical Shock Appearance : No abnormal exterior appearance Three shocks in each direct ion s hould be applied along
Capacitance Change Within ±10 % 3 mutually perpendicular axes of the test specimen (18 shocks)
Initial spec.
Initial Measurement 2*
Final Measurement 5*
Vibration Appearance : No abnormal exterior appearance 5g's for 20min., 12c ycles eac h of 3 orientat ions ,
Capacitance Change Within ±10 % Use 8"×5" PCB 0.031" Thick 7 secure points on one long side
Initial spec. and 2 secure points at corners of opposit e s ides. Parts mounted
within 2" from any secure point. Test from 10~2, 000 .
Initial Measurement 2*
Final Measurement 5*
Resistance to Appearance : No abnormal exterior appearance preheating : 150 for 60~120 sec .
Solder Heat Capacitance Change Within ±10 % Solder pot : 260±5 , 10± 1sec .
Initial spec. Initial Measurem ent 2*
Final Measurement 3*
ESD Appearance : No abnormal exterior appearance AEC-Q200-002 or ISO/DIS10605
Capacitance Change Within ±10 % Initial Measurement 2*
Initial spec. Final Measurement 4*
Solderability 95% of the term inat ions is t o be s oldered a) Preheat at 155 for 4 hours, I m m erse in s older f or 5s at 245± 5
evenly and continuous ly b) Steam aging for 8 hours, Immerse in solder for 5s at 245± 5
c) Steam aging for 8 hours, I m merse in solder for 120s at 260±5
solder : a solution et hanol and rosin
Electrical Capacit ance : Within spec ified tolerance *A capacitor prior to mea suring t he c apacitance is heat treated at
Characterization 0.1 max. 150 +0/-10 for 1hour and maint ained in ambient air f or 24±2 hours
IR(25 ) : More than 10,000 or 50 ×The Capacitance / D.F. should be m eas ured at 25 ,
W hic hever is smaller 1 ± 10%, 1 ± 0.2 Vrms
IR(125 ) More than 1,000 or 5 ×I.R. shou ld be meas ured with a DC voltage not exceeding
W hic hever is sm aller Rated Voltage @25 , @125 for 60~120 sec.
Dielectric Strength Dielectric Strength : 250% of t he rat ed voltage for 1~5 sec onds
Board Flex Appearance : No abnormal exterior appearance Bending to the limit, 3 for 60 sec onds 1*
Capacitance Change Within ±10 % Initial Measurement 2*
Final Measurement 5*
Terminal Appearance : No abnormal exterior appearance 2 N, for 60 sec.
Strength(SMD) Capacitance Change Within ±10 % Initial Measurement 2*
Final Measurement 5*
Beam Load Destruction value should be exceed 8 N Beam speed : 0.5±0.05 /sec
Temperature X7S
Characteristics From -55 to 125 , Capacitance change sh ould be within ±22% 1 ±10%, 0.1Vrm s
D. Recom m e nde d Solderi ng m e t hod :
Reflow ( Reflow Peak Temperature : 260 +0/-5 , 30sec. ), M eet IPC/J EDEC J-STD-020 D Standard
*1 : The figure indicates typical specification. Please refer to individual specifications.
*2 : Initial measurement : Perform a heat treatment at 150 +0/-10 for one hour after soldering process.
and then let sit for 24±2 hours at room temperature. Perform the initial measurem ent.
*3 : Final measurement : Let sit for 24±2 hours at room temperature after test conclusion, then measure.
*4 : Final measurement : Perform a heat treatm ent at 150 +0/-10 for one hour after soldering process.
and then let sit for 24±2 hours at room temperature. Perform the initial measurem ent.
*5 : Final measurement : Let measure within 24 hours at room temperature after test conclusion.
Product specifications included in the specifications are effective as of March 1, 2013.
Please be advised that they are standard product specifications for reference only.
We may change, modify or discontinue the product specifications without notice at any time.
So, you need to approve the product specifications before placing an order.
Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.
0.5ms Half sine 4.7m/ s ec
Performance Test condition
Peak value Duration W ave Velocity
1,500G
The products listed in this Specification sheet are NOT designed and manufactured for any use
and applications set forth below.
Please note that any misuse of the products deviating from products specifications or information
provided in this Spec sheet may cause serious property damages or personal injury.
We will NOT be liable for any damages resulting from any misuse of the products, specifically
including using the products for high reliability applications as listed below.
If you have any questions regarding this 'Limitation of Use and Application', you should first contact
our sales personnel or application engineers.
Aerospace/Aviation equipment
Medical equipment
Military equipment
Disaster prevention/crime prevention equipment
Power plant control equipment
Atomic energy-related equipment
Undersea equipment
Traffic signal equipment
Data-processing equipment
Electric heating apparatus, burning equipment
Safety equipment
Any other applications with the same as or similar complexity or reliability to the applications