SPECIFICATION
Supplier : Samsung electro-mechanics Samsung P/N : CL02B221KP2NNNC
Product : Multi-layer Ceramic Capacitor Description : CAP, 220㎊, 10V, ±10%, X7R, 01005
CL 02 B221 K P 2 N N N C
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 01005 (inch code) L: 0.4 ± 0.02 mm W: ± 0.02 mm
③Dielectric X7R ⑧Inner ele ctrode
④Capacitance 220 ㎊Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 10 V ⑩Special Reserved for future use
⑦Thickness 0.2 ± 0.02 mm ⑪Packaging Cardboard Type,7"reel
(20,000ea)
Sn 100%
Cu
Ni
0.2
A. Samsung Part Number
B. Samsung Reliability Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2Vrms
Tan δ (DF) 0.1 max.
Insulation More than 100Mohm㎌Rated Voltage 60~120 sec.
Resistance
Appearance No abnormal exterior appearance Visual inspection
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X7R
Characterisitcs (From -55℃ to 125℃, Capacitance change should be within ±15%)
Adhesive Strength No peeling shall be occur on the 100gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
Performance Test condition
250%
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0 hours
IR : More than 25㏁·㎌
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : More than 50㏁·㎌
1000+48/-0 hours
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
Product specifications included in this catalogue are effective as of March 1, 2013.
Please be advised that they are standard product specifications for reference only.
We may change, modify or discontinue the product specifications without notice at any time.
So,
y
ou need to approve the product specifications before placin
g
an order.
200%
Performance Test condition
Should you have any question regarding the product specifications,
please contact our sales personnel or application engineers.