SPECIFICATION * Samsung P/N : CL03C100GA3GNNH CAP, 10 , 25V, 2%, C0G, 0201 * Description : * Supplier : Samsung electro-mechanics * Product : Multi-layer Ceramic Capacitor A. Samsung Part Number Series Size Dielectric Capacitance CL 03 C 100 G A 3 G N N H Samsung Multi-layer Ceramic Capacitor 0201 (inch code) L: 0.6 0.03 10 2 % Rated Voltage Thickness 0.3 0.03 mm W: Inner electrode Termination C0G Capacitance tolerance mm Cu Cu Sn 100% Plating 25 V 0.3 0.03 mm (Pb Free) Product Special Normal Packaging Cardboard Type, 7" reel Reserved for future use B. Samsung Reliablility Test and Judgement condition Performance Within specified tolerance Test condition 110% 0.5~5Vrms Rated Voltage 60~120 sec. Resistance 10,000Mohm or 500Mohm Whichever is Smaller Appearance No abnormal exterior appearance Withstanding No dielectric breakdown or Microscope (x10) 300% of the rated voltage Voltage mechanical breakdown Temperature C0G Characterisitcs Adhesive Strength (From -55 to 125, Capacitance change shoud be within 30PPM/) No peeling shall be occur on the 200gF, for 101 sec. of Termination terminal electrode Bending Strength Capacitance change : Bending to the limit (1mm) with 1.0mm/sec. Solderability within 5% or 0.5 whichever is larger More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 2455, 30.3sec. Capacitance 600 min Q Insulation (preheating : 80~120 for 10~30sec.) Resistance to Capacitance change : Soldering heat within 2.5% or 0.25 whichever is larger Tan , IR : initial spec. Solder pot : 2705, 101sec. Performance Test condition Vibration Test Capacitance change : Moisture within 2.5% or 0.25 whichever is larger From 10 to 55 (return : 1min.) Tan , IR : initial spec. 2hours x 3 direction (x, y, z) Capacitance change : With rated voltage Resistance Amplitude : 1.5mm within 7.5% or 0.75 whichever is larger 402, 90~95%RH, 500+12/-0hrs Q: 133.33 min IR : 500Mohm or 25Mohm Whichever is Smaller High Temperature Capacitance change : With 200% Resistance within 3% or 0.3 whichever is larger Q: 300 min Max. operating temperature IR : of the rated voltage 1000+48/-0hrs 1000Mohm or 50Mohm Whichever is Smaller Temperature Capacitance change : 1 cycle condition Cycling 25 within 2.5% or 0.25 whichever is larger Min. operating temperature Tan , IR : initial spec. Max. operating temperature 25 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5, 10sec. Max ) * For the more detail Specification, Please refer to the Samsung MLCC catalogue.